![](/en/data/attachment/201906/14/e4fc53dbbe773860b877749add508c5a.png)
Grey-white
Origin: Shandong, China
Carrier: PE/PP
Calcium oxide content: 75%-80%
Colour: White/Grey/Black
Water absorption: ≥20%
Melting index 21.6KG/200℃: 5-40ɡ/10min
Solution temperature: 140℃-220℃
Phase fusibility: PE/PP/PVC/ABS
Origin: Shandong, China
Carrier: PE/PP
Calcium oxide content: 75%-80%
Colour: White/Grey/Black
Water absorption: ≥20%
Melting index 21.6KG/200℃: 5-40ɡ/10min
Solution temperature: 140℃-220℃
Phase fusibility: PE/PP/PVC/ABS
Defoaming masterbatch (also known as dehumidifying masterbatch and absorbent masterbatch) is suitable for the production enterprises of PE and PP damp raw materials and recycled plastic products. The raw materials contain trace moisture or moisture, which has a very serious impact on the production of plastic products. Therefore, enterprises generally use drying equipment to dry plastic, which is a great waste of energy and human resources, and increases the life of products. The cost of production, and the use of this defoaming masterbatch, only need to be added to the raw material to mix evenly, without any adjustment of the production process of the product, can eliminate all the problems caused by water bubbles, moire, cracks, spots and so on.
Usage method:
When the defoaming masterbatch is stirred with the moisture-affected plastic material directly, the product can be processed and produced. For example, the proportion of defoaming masterbatch added is 1%-2% for blown film production. If used in sheet and injection moulding production, the addition ratio is 2%-5%. If used in pipe production, add 2%-5%. Specific addition proportion should be added at the discretion of users according to the moisture condition of plastics.
Matters needing attention:
1. Avoid dampness and water absorption before using this masterbatch.
2. The best ingredient is used before use.
3. Do not heat and dry with damp plastics, so as not to cause poor quality in processing.
4. Check the package before opening the package, and heat-seal the unused masterbatch as soon as possible.
Physical properties:
Defoaming Masterbatch |
|
Index |
Numerical value |
Carrier |
PE/PP |
Colour |
White/Grey/Black |
Calcium oxide content |
75%-80% |
Melting index 21.6KG/200℃ |
5-40ɡ/10min |
Water absorption |
≥20% |
Solution temperature |
140℃-200℃ |
Phase fusibility |
PE/PP/PVC/ABS |
Applications:
Drainage pipes, moulding products, bag products, sheet products, film blowing, blow moulding products and injection moulding products.
Packing:
Vacuum packing, 1KG, 2.5KG, 5KG, 25KG per box. Damage and open storage are strictly prohibited to avoid sun exposure and rain.
159-5477-9199
0531-82968527
zjc@hxsjsd.com
www.hxsjsd.com
88 North Qingxu Road, Xuyuanzi Township, Qingyun County, Dezhou City, Shandong Province